This Specialty family provides unique filaments from Polymaker to unlock new 3D printing applications.
PolyWood
PolyWood™ is made entirely with PLA using a special foaming technology. It exhibits the same density and appearance as wood. PolyWood™ is a wood mimic filament without actual wood powder, which removes all risks of nozzle clogs.
Because the polywood contains no wood, it is possible to combine any colour with the material. The printed parts have an amazing surface finish and the visual layering is minimized. More colours and materials are already under development.
Polywood ™ is the only 3D printable foam to date. The density of Polywood is on average 0.8 g / cm3, which is about 35 - 40% less than PLA. Due to the low density, the component has a lower weight.
Recommended Settings
- Nozzle Temperature: 190˚C – 210˚C
- Printing Speed: 30mm/s – 50mm/s
- Bed Temperature: 25˚C – 60˚C
- Bed Surface: Glass with glue, blue tape, BuilTak®
- Cooling Fan: ON
Basic Data Printing Parameter
| Filament Typ | Wood |
| Diameter | 1,75 mm |
| Weight | 0,6 kg |
| Lenght | 312 m |
| Color | Brown wood |
| Recomended Printing Temp Min | 190 ºC |
| Recomended Printing Temp Max | 210 ºC |
| Recomended Printbed Temperature Min | 25 ºC |
| Recomended Printbed Temperature Max | 60 ºC |
| Recomended Printing Speed Min | 30 mm/s |
| Recommended Printing Speed Max | 50 mm/s |
| Recomended Retraction Min | 3 mm |
| General | |
| Specific gravity | 0,8 g/cm3 ISO 1183 |
| Temperature | |
| Vicat softening temp | 60 °C ISO 306 |
| Heat deflection temp | 54,1 °C ISO 75 |
| Tensile | |
| Tensile strength | 23,2 MPa ISO 527 |
| Tensile modulus | 2636 MPa ISO 527 |
| Flexural | |
| Flexural Strenght | 52,9 MPa ISO 178 |
| Flexural Modulus | 2607 MPa ISO 178 |
| Other | |
| Impact Strength | 2,1 KJ/m2 ISO 179 |