PolyMax
PolyMax™ is a family of advanced 3D printing filaments produced with Polymaker’s Nano-reinforcement technology, to deliver exceptional mechanical properties and printing quality.
PC-FR
PolyMax™ PC-FR, creation from Covestro’s Makrolon® family, could achieve V0 performance in the UL94 flame retardancy test and displays excellent toughness, strength and heat resistance. This filament opens new applications in the automotive, railway and aerospace industries.
Recommended Settings
- Nozzle Temperature: 250˚C – 270˚C
- Printing Speed: 30 – 50mm/s
- Bed Temperature: 90˚C – 105˚C
- Chamber Temperature: 90˚C – 100˚C
- Bed Surface: almost any surface with a thin coat of MAGIGOO PC
- Cooling Fan: OFF
Note: When printing with PolyMax™ PC-FR it is recommended to use a heated chamber. It is recommended to anneal the printed part right after the printing process to release the residual internal stress when not using a heated chamber. Annealing settings: 90˚C for 6h
Basic Data Printing Parameter
| Filament Typ | PC |
| Diameter | 2,85 mm |
| Weight | 1,00 kg |
| Lenght | 131 m |
| Color | White |
| Recomended Printing Temp Min | 250 ºC |
| Recomended Printing Temp Max | 270 ºC |
| Recomended Printbed Temperature Min | 90 ºC |
| Recomended Printbed Temperature Max | 105 ºC |
| Recomended Printing Speed Min | 30 mm/s |
| Recommended Printing Speed Max | 50 mm/s |
| Recomended Fan Speed Min | 0 % |
| Recomended Fan Speed Max | 0 % |
| Recomended Retraction Min | 1 mm |
| Recomended Retraction Max | 20 mm |
| General | |
| Specific gravity | 1,2 g/cm3 ISO 1183 |
| Temperature | |
| Vicat softening temp | 116 °C ISO 306 |
| Heat deflection temp | 107 °C ISO 75 |
| Tensile | |
| Tensile strength | 67 MPa |
| Tensile modulus | 2634 MPa |
| Flexural | |
| Flexural Strenght | 96,6 MPa ISO 178 |
| Flexural Modulus | 2518 MPa ISO 178 |
| Other | |
| Impact Strength | 11,7 KJ/m2 ISO 179 |
Polymaker Polymax PC-FR